    Influence of fractional carbon-dioxide laser in comparison to ErCr-YSGG on the dentin bond integrity of bioactive materials.

    • Zaid Al-Jeaidi.
    • Zaid Al-Jeaidi Associate Professor, Conservative Dental Science Department, College of Dentistry, Prince Sattam Bin Abdulaziz University, Al-Kharj, Saudi Arabia.
    • Pak J Med Sci. 2020 Mar 1; 36 (3): 526-531.

    ObjectiveThe aim was to assess the influence of Er, Cr: YSGG laser (ECL) and fractional carbon dioxide laser (FCL) on the shear bond strength (SBS) and microleakage of bioactive restorative material to dentin.MethodsThe study was performed in King Saud university in the month of June-July 2019. One hundred and twenty permanent teeth were vertically placed in acrylic resin. Based on the type of surface treatment regime (n=40), samples were divided into three groups. Group-I samples were surface conditioned with total etch and rinse (TE); Group-2 samples were surface treated with Er, Cr: YSGG laser (ECL) and Group-3 specimens were conditioned with fractional carbon dioxide laser (FCL). Surface treatment of dentin was followed by type of bulk fill resin (BFR) application. Tetric-N-Ceram was bonded to dentin conditioned with TE (n=20), FCL (n=20) and ECL (n=20). Similarly, bioactive material (BAM) was also bonded to conditioned surface (n=60). Samples (n=10) among each group were placed in a Universal testing machine. For microleakage testing 5 pairs of samples from each group (n=10) were placed in solution of 2% methylene blue for 24h Fracture analysis was performed using stereomicroscope at 40x magnification. Descriptive statistics i.e., means and standard for SBS and microleakage were compared using analysis of variance (ANOVA) and Tukey's post hoc test at a significance level of (p < 0.05).ResultsThe highest SBS scores were displayed by TE-BFR (Bulk filled resin) (19.21 ± 0.925 Mpa) and the lowest shear bond scores were presented by FCL-BFR (11.06±1.611 Mpa). The lowest microleakage scores were exhibited by group ECL-BFR (24.11±13.01nm). Similarly, the highest microleakage score was displayed in group FCL-BAM (42.18±16.32 nm). Admixed failure was pertinent in groups conditioned by ECL. Moreover, groups conditioned with FCL adhesive type of failure was found in abundance.ConclusionsECL has a potential to be used as an alternate to total etch and rinse for conditioning of dentin when bonded to bioactive materials.Copyright: © Pakistan Journal of Medical Sciences.

      Pubmed     Copy Citation     Plaintext  

      Add institutional full text...

    Notes

     
    Knowledge, pearl, summary or comment to share?
    300 characters remaining
    help        
    You can also include formatting, links, images and footnotes in your notes
    • Simple formatting can be added to notes, such as *italics*, _underline_ or **bold**.
    • Superscript can be denoted by <sup>text</sup> and subscript <sub>text</sub>.
    • Numbered or bulleted lists can be created using either numbered lines 1. 2. 3., hyphens - or asterisks *.
    • Links can be included with: [my link to pubmed](http://pubmed.com)
    • Images can be included with: ![alt text](https://bestmedicaljournal.com/study_graph.jpg "Image Title Text")
    • For footnotes use [^1](This is a footnote.) inline.
    • Or use an inline reference [^1] to refer to a longer footnote elseweher in the document [^1]: This is a long footnote..

    hide…