• Joon Ho Seo, Sol Moi Park, Beom Joo Yang, and Jeong Gook Jang.
• Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology, 291 Daehak-ro, Youseong-gu, Daejeon 34141, Korea. junhoo11@kaist.ac.kr.
• Materials (Basel). 2019 Apr 23; 12 (8).

AbstractThe present study prepared calcined oyster shell powder having chemical composition and crystal structure of calcium oxide and lime, respectively, and investigated the fresh and hardened properties of cement mortar incorporating calcined oyster shell powder as an additive. The test results indicated that the hydration of calcined oyster shell powder promoted the additional formation of Ca(OH)2 at the initial reaction stage, thereby increasing the heat of hydration. In particular, the volumetric increase of calcined oyster shell powder during hydration compensated the autogenous shrinkage of mortar at early ages, ultimately leading to a clear difference in the shrinkage values at final readings. However, an excessive incorporation of calcined oyster shell powder affected the rate of C-S-H formation in the acceleratory period of hydration, resulting in a decrease in the compressive strength development. Meanwhile, the degree of flow loss was inconsequential and rapid flow loss was not observed in the specimens with calcined oyster shell powder. Therefore, considering the fresh and hardened properties of cement mortar, the incorporation of calcined oyster shell powder of approximately 3% by weight of cement is recommended to enhance the properties of cement mortar in terms of compressive strength and autogenous shrinkage.

2 keywords...

hide…