• Davide Cortellini, Angelo Canale, Rodrigo O A Souza, Fernanda Campos, Julia C Lima, and Mutlu Özcan.
• Private Practice, Riccione, Italy.
• J Prosthodont. 2015 Dec 1; 24 (8): 615-9.

PurposeThe aim of this study was to evaluate the durability of lithium disilicate crowns bonded on abutments prepared with two types of finish lines after long-term cyclic loading.Materials And MethodsPressed lithium disilicate all-ceramic molar crowns were bonded (Variolink II) to epoxy abutments (height: 5.5 mm, Ø: 7.5 mm, conicity: 6°) (N = 20) with either knife-edge (KE) or large chamfer (LC) finish lines. Each assembly was submitted to cyclic loading (1,200,000×; 200 N; 1 Hz) in water and then tested until fracture in a universal testing machine (1 mm/min). Failure types were classified and further evaluated under stereomicroscope and SEM. The data (N) were analyzed using one-way ANOVA. Weibull distribution values including the Weibull modulus (m), characteristic strength (0), probability of failure at 5% (0.05), 1% (0.01), and correlation coefficient were calculated.ResultsType of finish line did not significantly influence the mean fracture strength of pressed ceramic crowns (KE: 1655 ± 353 N; LC: 1618 ± 263 N) (p = 0.7898). Weibull distribution presented lower shape value (m) of KE (m = 5.48; CI: 3.5 to 8.6) compared to LC (m = 7.68; CI: 5.2 to 11.3). Characteristic strengths (0) (KE: 1784.9 N; LC: 1712.1 N) were higher than probability of failure at 5% (0.05) (KE: 1038.1 N; LC: 1163.4 N) followed by 1% (0.01) (KE: 771 N; LC: 941.1 N), with a correlation coefficient of 0.966 for KE and 0.924 for LC. Type V failures (severe fracture of the crown and/or tooth) were more common in both groups. SEM findings showed that fractures occurred mainly from the cement/ceramic interface at the occlusal side of the crowns.ConclusionLithium disilicate ceramic crowns bonded onto abutment teeth with KE preparation resulted in similar fracture strength to those bonded on abutments with LC finish line.Clinical SignificancePressed lithium disilicate ceramic crowns may not require invasive finish line preparations since finish line type did not impair the strength after aging conditions.© 2015 by the American College of Prosthodontists.

10 keywords...

hide…