• Niger J Clin Pract. 2021 Oct 1; 24 (10): 1442-1449.

BackgroundResidual monomers released from composite resins have cytotoxic, mutagenic, and estrogenic effects. Mode of polymerization and application thickness are important for monomer release.AimsThe aim of this study was to investigate the effects of different modes of a third-generation light-curing unit (LCU) and layer thickness on residual monomer released from two different bulk-fill composite resins. A total of 80 samples were prepared for each bulk-fill composite using a mold. Each bulk-fill composite was divided into four groups according to polymerization mode (standard and extra power) and layer thickness (2 and 4 mm). In addition, four groups were divided into four subgroups according to time periods (1 h, 24 h, 3 days, and 7 days).Methods And MaterialThe samples were polymerized with VALO LED device. The amount of residual monomer was measured with High-Performance Liquid Chromatography (HPLC). All statistical analyses were processed using SPSS Version 23.0. The normal distribution of data was confirmed using Kolmogorov-Smirnov Normal Distribution Test and Shapiro-Wilk Normal Distribution Test. When the distribution was normal, parametric tests, Student's t test and one-way ANOVA, were used. When the distribution was not normal, non-parametric tests, Mann-Whitney U test, and Kruskal-Wallis testwere used.ResultsIt was found that the standard mode of LCU produced lower amounts of TEGDMA, Bis-GMA, and UDMA in both composite materials. In addition, when the layer thickness increased, TEGDMA, Bis-GMA, and UDMA releases increased, too.ConclusionsThis study revealed that the amount of residual monomers released from bulk-fill composites was affected by layer thickness and polymerization time.

8 keywords...

hide…