AimThis study aims to comparatively evaluate the flexural strength, internal adaptation, elastic modulus, and maximum deflection of a newly introduced, strengthened injection-molded semi-flexed polyamide resin (Deflex) and a conventional heat-cured resin containing cross-linking polymethyl methacrylate denture base polymers (QC-20).Materials And MethodsA vinyl polysiloxane film replicating the gap between the denture base and the metallic master model of an edentulous maxilla was weighed using an analytical balance with an accuracy of 0.0001 g for the measurement of internal adaptation. The measurements were performed immediately after surface finishing. Seven rectangular test samples measuring 65 × 10 × 3.3 mm3 were set up for flexural strength test. Flexural strength test (three-point bending test) was performed using a universal machine under axial load at a crosshead speed of 5 mm/min. One-way ANOVA (α = 0.05) following by t tests was utilized in statistical analysis.ResultsThe difference between the flexural strength of the denture base resins of Deflex and QC-20 was found to be statistically significant. The injection-molded resin demonstrated better internal adaptation compared to the conventional heat-polymerized resin. Evaluation of the physical test results revealed that the polyamide samples were more flexible than polymethyl methacrylate and did not break during flexural strength tests.ConclusionSome properties of denture base resins, such as resin types, internal adaptation, and mechanical strength, may play a significant role in clinical performance of complete dentures and removable partial prostheses. Because of the superior flexural strength properties and internal adaptation characteristics, Deflex may prove to be a useful alternative to conventional denture base resin.

7 keywords...

hide…