AbstractThe purpose of this study was to evaluate the mid-term clinical results and polyethylene wear of vitamin E-diffused highly cross-linked polyethylene (HXLPE) and 2-methacryloyloxyethyl phosphorylcholine (MPC)-grafted HXLPE in cementless total hip arthroplasty (THA). Thirty-four THAs with vitamin E-diffused HXLPE (VEPE) and 32-mm cobalt-chromium head, and 116 THAs with MPC-grafted HXLPE and 32-mm alumina head were evaluated. The Merle d'Aubigné and Postel scores were administered. Kaplan-Meier survivorship was analyzed. Annual radiographs were analyzed using computerized method and linear steady-state wear rate was measured. The mean duration of follow-up was 9 years (range, 7-11 years) in VEPE group and 8 years (range, 7-10 years) in MPC group. The mean Merle d'Aubigné and Postel scores improved postoperatively in both groups. Kaplan-Meier survivorship with endpoint of revision was 100% (95% confidence interval, 100%-100%) in VEPE group and 98.3% (95% confidence interval, 93.4%-99.6%) in MPC group at 10 years (P = .44). The mean steady-state wear rate was 0.007 mm/year in VEPE group and 0.006 mm/year in MPC group (P = .60). The clinical results of both groups were good and wear rates of both liners were very low.Copyright © 2023 the Author(s). Published by Wolters Kluwer Health, Inc.

12 keywords...

hide…