• F S Kleinstueck, C J Diederich, W H Nau, C M Puttlitz, J A Smith, D S Bradford, and J C Lotz.
• Department of Orthopaedic Surgery, University of California at San Francisco, 94143-0514, USA.
• Spine. 2001 Oct 15; 26 (20): 2198-207.

Study DesignHuman cadaver lumbar spines were used to assess the acute effects of intradiscal electrothermal therapy in vitro.ObjectiveTo determine whether intradiscal electrothermal therapy produces acute changes in disc histology and motion segment stability.Summary Of Background DataIntradiscal electrothermal therapy has been introduced as an alternative for the treatment of discogenic low back pain. Several hypothesized mechanisms for the effect of intradiscal electrothermal therapy have been suggested including shrinkage of the nucleus or sealing of the anulus fibrosus by contraction of collagen fibers, and thermal ablation of sensitive nerve fibers in the outer anulus.MethodsIntradiscal electrothermal therapy was performed with the Spinecath by Oratec on 19 fresh, frozen human lumbar cadaver specimens. In a separate study, eight specimens were tested biomechanically and instrumented to map the thermal distribution, whereas five specimens were tested only biomechanically, both before and after intradiscal electrothermal therapy. Six additional specimens were heated with intradiscal electrothermal therapy, and the resulting canal was backfilled with a silicone rubber compound to allow colocalization of the catheter and anular architecture.ResultsA consistent pattern of increased motion and decreased stiffness was observed. For the specimens in which only biomechanical measurements were taken, a 10% increase in the motion, on the average, at 5 Nm torque was observed after intradiscal electrothermal therapy. No apparent alteration of the anular architecture was observed around the catheter site in the intradiscal electrothermal therapy-treated discs.ConclusionThe data from this study suggest that the temperatures developed during intradiscal electrothermal therapy are insufficient to alter collagen architecture or stiffen the treated motion segment acutely.

32 keywords...

hide…